I think it's a safety issue. Say you live in a salt mine in London. If your ground for the ABS pump gets corroded prematurely, you'd have a nice lawsuit if an accident occurs. If it were marketing it would not be unadvertised. Stereo equipment sales thrive on the the fact that it's gold plated, SVX sales do not.
|
I would reckon that that a decent thickness of cadmium or zinc would be better, as this would be more likely to resist possible mechanical damage in transit, storage, or during installation.